The PE fabric is made from close to a thousand UHMWPE fibers with cut-edge technology and is the main use by personal protective manufacturers.
Menu
The PE fabric is made from close to a thousand UHMWPE fibers with cut-edge technology and is the main use by personal protective manufacturers.
Guodun Armor has a Successful show at IDEX2015 during 21-25 FEB, 2015 in Abu Dhabi, UAE.
Guodun Armor has a Successful show at IDEX2017 during 21-25 FEB, 2017 in Abu Dhabi, UAE.
Test Sample 27 Layers SB160 UHMWPE UD (without foam at back) Test Standard GA141-2010 level 2 (compare to NIJ 0101.06 IIIA) Test Ammunition 7.62x25mm Lead Core x 6 shots Test By China Ordnance Equipment Test Center Test Time 2022.11 Test Result All passed testing (Sample Condition: 60 Degrees Temperature) Test report of bulletproof fabric SB160 27 Layers 60 degrees Distance Angle Shooting Sequence Muzzle Velocity (m/s) Penetration BFS Requirement BFS depth 5M 0 1 447 no <=25mm 25mm 5M 0 2 451 no <=25mm 23mm 5M 0 3 448 no <=25mm 21mm
Test Sample 25 Layers SB160 UHMWPE UD (without foam at back) Test Standard GA141-2010 level 2 (compare to NIJ 0101.06 IIIA) Test Ammunition 7.62x25mm Lead Core x 6 shots Test By China Ordnance Equipment Test Center Test Time 2022.11 Test Result All passed testing (Sample Condition: Normal Temperature) Test report of bulletproof fabric SB160 25 Layers Distance Angle Shooting Sequence Muzzle Velocity (m/s) Penetration BFS Requirement BFS depth 5M 0 1 453 no <=25mm 24mm 5M +30 2 442 no <=25mm 18mm 5M -45 3 449 no <=25mm 20mm 5M 0 4 454 no <=25mm 22mm 5M 0 5 454 no <=25mm 23mm 5M 0 6 448 no <=25mm 25mm
Test Sample 35 Layers SB130 UHMWPE UD (without foam at back) Test Standard GA141-2010 level 2 (compare to NIJ 0101.06 IIIA) Test Ammunition 7.62x25mm Lead Core x 6 shots Test By China Ordnance Equipment Test Center Test Time 2022.11 Test Result All passed testing (Sample Condition: After -40 Degrees Temperature) Test report of bulletproof fabric SB130 35 Layers -40 Degrees Distance Angle Shooting Sequence Muzzle Velocity (m/s) Penetration BFS Requirement BFS depth 5M 0 1 443 no <=25mm 24mm 5M 0 2 452 no <=25mm 23mm 5M 0 3 451 no <=25mm 20mm
Test Sample 37 Layers SB130 UHMWPE UD (without foam at back) Test Standard GA141-2010 level 2 (compare to NIJ 0101.06 IIIA) Test Ammunition 7.62x25mm Lead Core x 6 shots Test By China Ordnance Equipment Test Center Test Time 2022.9 Test Result All passed testing (Sample Condition: Normal Temperature) Test report of bulletproof fabric SB130 37 Layers Distance Angle Shooting Sequence Muzzle Velocity (m/s) Penetration BFS Requirement BFS depth 5M 0 1 443 no <=25mm 18mm 5M +30 2 443 no <=25mm 19mm 5M -45 3 444 no <=25mm 21mm 5M 0 4 452 no <=25mm 21mm 5M 0 5 448 no <=25mm 20mm 5M 0 6 447 no <=25mm 21mm
Test Sample 35 Layers SB130 UHMWPE UD (without foam at back) Test Standard GA141-2010 level 2 (compare to NIJ 0101.06 IIIA) Test Ammunition 7.62x25mm Lead Core x 6 shots Test By China Ordnance Equipment Test Center Test Time 2022.10 Test Result All passed testing (Sample Condition: Normal Temperature) Test report of bulletproof fabric SB130 35 Layers Distance Angle Shooting Sequence Muzzle Velocity (m/s) Penetration BFS Requirement BFS depth 5M 0 1 443 no <=25mm 19mm 5M +30 2 454 no <=25mm 21mm 5M -45 3 452 no <=25mm 22mm 5M 0 4 450 no <=25mm 21mm 5M 0 5 451 no <=25mm 24mm 5M 0 6 447 no <=25mm 22mm
Made by polyester 600D, adjustable one size fit all, weight around 0.8kg/pc
The 600D polyester with PVC coat for anti-flame testing in 2019 Item Unit Result Value Standard Area Density g/m2 465 GB/T 4669-2008 Tensile Strength N Warp 1800 GB/T 3923.1-1997 Tensile Strength N Weft 1390 GB/T 3923.1-1997 Tearing Strength N Warp 132 GB/T 3917.3-2009 Tearing Strength N Weft 94 GB/T 3917.3-2009 Waterproof kPa >100 FZ/T 01004-2008 Anti Flame Length mm Warp 90 GB/T 5455-1997 Anti Flame Length mm Weft 97 GB/T 5455-1997 Anti Flame Time s Warp 13.5 GB/T 5455-1997 Anti Flame Time s Weft 7.4 GB/T 5455-1997